PRODUCT PARAMETERS
Appearance : No visible cracks, holes, glaze peeling, or obvious color difference on the product
Dimensional Tolerance (Sheet Material) : Length/mm : +0.6
Width/mm ：+0.9
Thickness/% ：7.0
Edge Straightness/% ：0
Squareness/% ：0
Areal Density Deviation/ (kg/m²) : +0.1
Salt Spray Resistance (500h) : No anomalies
Hazardous Substance Emission/[mg/(m²·h)] : Total Volatile Organic Compounds(TVOC) ：0.14
Formaldehyde ：0.035
Water Vapor Permeability Density/[g/(m²·h)] : 1.46
Radioactive Nuclide Limit (Class A Decoration Material) : Internal Irradiation Index IRa ：0.41
External Irradiation Index Iγ ：0.35
Flexibility (10mm-diameter mandrel) : No cracks on the sample after the bending test with a 10mm-diameter mandrel
Water Absorption/% : 7
Flexibility (100mm-diameter cylinder) : No cracks on the sample
Heating Dimensional Change Rate/% : Longitudinal ：0.15
Transverse ：0.13
Temperature Resistance(10 cycles) : Appearance : No abnormality in the sample
Flexibility : No cracks on the sample
Artificial Weathering Resistance (1600h) : Appearance : No anomalies
Chalking/Grade : 0
Discoloration/Grade : 0
Flexibility : No cracks on the sample
Stain Resistance/Grade : 1
Chemical Corrosion Resistance : No visible impairment after testing
Water Absorption/% : 7
Flexibility (100mm-diameter cylinder) : No cracks on the sample
Heating Dimensional Change Rate/% : Longitudinal : 0.15
Transverse : 0.13
Temperature Resistance(10 cycles) : Appearance : No abnormality in the sample
Flexibility : No cracks on the sample
Artificial Weathering Resistance (1600h) : Appearance : No anomalies
Chalking/Grade : 0
Discoloration/Grade : 0
Flexibility : No cracks on the sample
Stain Resistance/Grade : 1
Chemical Corrosion Resistance : No visible impairment after testing
Flame Retardancy (Class B₁) :
Fire Growth Rate Index FIGRA₀.₂MJ, W/s : 39
Total Heat Release in 600s THR₆₀₀s, MJ : 0.8
Lateral Flame Spread Length (LFS) : Did not reach the long side edge of the sample
Flame Height (Edge ignition for 30s, mm) : Complies with the requirements
Flame Height (Surface ignition for 30s, mm) : Complies with the requirements
ping material igniting filter paper (Edge ignition for 30s) : No burning drips within 60 seconds
Dripping material igniting filter paper (Surface ignition for 30s) : No burning drips within 60 seconds
Smoke Production Rate Index SMOGRA, m²/S² : s1 & s2 : 5
Total Smoke Production in 600s TSP₆₀₀s, ㎡ : s1 & s2 : 39
Burning Drips/Particles : Burning drips/particles occurred within 600 seconds, with a duration not exceeding 10 seconds
APPLICATION METHOD